| Resin PVC | SG3 | SG5 | SG8 | |
| Viskositas, ml/g (atau nilai K) | 135-127 (72-71) 1350-1250 | 118-107 (68-66) 1100-1000 | 86-73 (59-55) 750-650 | |
| Jumlah partikel pengotor≤ | 30 | 30 | 40 | |
| Konten yang mudah menguap %,≤ | 0.40 | 0.40 | 0.40 | |
| Muncul kepadatan g/ml≥ | 0.42 | 0.45 | 0.45 | |
| Residu Setelah Saringan | 0.25 mm, ≦ | 2.0 | 2.0 | 2.0 |
| 0.063 mm, ≥ | 90 | 90 | 90 | |
| Jumlah butir/400cm2≤ | 40 | 40 | 50 | |
| Nilai serap plasticizer 100g resin g≥ | 25 | 17 | - | |
| Keputihan %,≥ | 75 | 75 | 70 | |
| Konduktivitas larutan ekstraktan air, us/(cm.g)】≤ | 5 | - | - | |
| Kandungan sisa klor thylene mg/kg≤ | 10 | 10 | 10 | |
| Residu Ethyidenediklorideug/g | 150 | 150 | 150 | |
| PVC RESIN SG3 | ||||
| Barang | Spesifikasi | Nilai yang terukur | ||
| Kelas Unggul | Kelas satu | Kelas Berkualitas | ||
| Nomor Viskositas, ML/G | 127 ~ 135 | 127 ~ 135 | 127 ~ 135 | 131 |
| Fraksi massa Materi Volatil (termasuk air) | ≤0.3% | ≤0.4% | ≤0.5% | ≤0.2% |
| Kepadatan Semu, g/mL | ≥ 0.45 | ≥ 0.42 | ≥ 0.4 | ≥ 0.51 |
| Kurangi onSieve, 250μmSieve mesh≤Sieve | 1.6% | 2% | 8% | 0.9% |
| Kurangi Saringan, 63μmSaringan mesh≥Saringan | 97% | 90% | 85% | 99% |
| “Mata Ikan”/400cm2≤ | 20 | 30 | 60 | 10 |
| Keputihan (160 ° C, 10 menit) ≥ | 78% | 75% | 70% | 83% |
| Penyerapan Pemlastis Resin 100g, g≥ | 26 | 25 | 23 | 27 |
| Nomor Partikel Pengotor ≤ | 16 | 30 | 60 | 12 |
| Konduktivitas ekstrak air, uS/cm.g ≤ | 5 | 5 | --- | 0.6 |
| Kandungan Residu Vinyl Klorida Monomer,ug/g≤ | 5 | 5 | 10 | 1.6 |
| PVC RESIN SG5 | ||||
| Barang | Spesifikasi | Nilai yang terukur | ||
| Kelas Unggul | Kelas satu | Kelas Berkualitas | ||
| Nomor Viskositas, ML/G | 118 ~ 107 | 111.24 | ||
| Fraksi massa Materi Volatil (termasuk air) | ≤0.4% | ≤0.4% | ≤0.5% | ≤0.4% |
| Nomor partikel pengotor ≤ | 16 | 30 | 80 | 16 |
| Kepadatan Semu, g/mL | ≥ 0.48 | ≥ 0.45 | ≥ 0.42 | ≥ 0.519 |
| Kurangi onSieve, 250μmSieve mesh≤Sieve | 2% | 2% | 8% | 0.9% |
| Kurangi Saringan, 63μmSaringan mesh≥Saringan | 95% | 90% | 85% | 98% |
| “Mata Ikan”/400cm2≤ | 20 | 40 | 90 | 8 |
| Keputihan (160 ° C, 10 menit) ≥ | 78% | 75% | 70% | 81.39% |
| Penyerapan Pemlastis Resin 100g, g≥ | 19 | 17 | --- | 22.28 |
| Kandungan Residu Vinyl Klorida Monomer,ug/g≤ | 5 | 10 | 30 | 1 |
| PVC RESIN SG8 | |
| Barang | Spesifikasi |
| Nomor Viskositas, ML/G | 73-86 |
| Nomor Partikel Pengotor ≤ | 20 |
| Fraksi massa Bahan Mudah Menguap (termasuk air) ≤ | 0.4% |
| Kepadatan Semu, g/mL≥ | 0.52 |
| Kurangi onSieve, 250μmSieve mesh≤Sieve | 1.6% |
| Kurangi Saringan, 63μmSaringan mesh≥Saringan | 97% |
| “Mata Ikan”/400cm2≤ | 30 |
| Penyerapan Pemlastis Resin 100g, g≥ | 12 |
| Keputihan (160 ° C, 10 menit) ≥ | 75% |
| Kandungan sisa Vinyl Klorida Monomer,mg/l≤ | 5 |
Aplikasi:
Interior mobil, bahan dekoratif keluarga, kotak lampu iklan, sol sepatu, pipa PVC, profil PVC, lembaran dan pelat PVC, film bergulir, mainan tiup, produk luar ruangan, kawat dan kabel PVC, kulit buatan PVC, lantai kayu dan plastik, papan bergelombang , dll.
PVC SG-3untuk film, selang, kulit, kabel kawat dan produk lunak keperluan umum lainnya
PVC SG-5untuk pipa, fitting, panel, kalender, injeksi, moulding, profil dan sandal.
PVC SG-7/SG-8untuk botol, lembaran, kalender, injeksi kaku, dan pipa cetakan.
Hak Cipta © Richest Group Seluruh Hak Dilindungi Undang-Undang
EN 
AR 
NL 
FR 
DE 
EL 
HI 
IT 
JA 
KO 
PL 
PT 
RO 
RU 
ES 
TL 
ID 
UK 
VI 
SQ 
MT 
TH 
TR 
FA 
AF 
MS 
SW 
KA 
UR 
BN 
LO 
NE 
SO 
TA 
ZU 
MY 
KK 
SI 
TG 
KU 
XH 